Ultrafiltration (UF) is widely applied in different separation processes in the pulp and paper industry. The growing need to protect the environment, a lack of pure water and an interest in producing high-value chemicals from compounds present in process waters will probably lead to an increase in the use of UF in the pulp and paper industry. The efficiency and cost-effectiveness of a UF process depends on the applied membrane. The membrane should have a high and stable filtration capacity, a particular selectivity and a long operational lifetime. To meet these requirements a membrane should have a low fouling tendency. In addition, it should withstand the prevailing operational and chemical conditions. This thesis evaluates the performance and applicability of the regenerated cellulose (RC) membranes 00030T and C2 in the treatment of pulp and paper mill process waters based on the requirements above. The results demonstrated that both the tested RC membranes fulfilled well the requirement of high filtration capacity. In addition, in the filtration of a paper mill clear filtrate (CF) the RC membranes were not as greatly affected by variations in the CF quality as a polysulphone membrane. Furthermore, due to their extreme hydrophilicity and weak charge the fouling tendency of the membranes can be expected to be low in pulp and paper mill filtration applications. It is, however, known that fouling cannot be totally avoided even when the membrane is chosen very carefully. This study indicated that carbohydrates influenced negatively on permeability and caused fouling in the filtration of groundwood mill circulation water. Thus, a pre-treatment effectively reducing the amount of carbohydrates might help to maintain a stable capacity. However, the results of the thesis also showed that the removal of some of the possible foulants might just increase the harmful effect of others. Multivariate examination was useful in the understanding of the complicated factors causing the unstable capacity. The thesis also revealed that the 00030T and C2 membranes can be used at high pressure (max. tested pressure 12 bar). The C2 membrane, having a sponge-like substructure, was more pressure resistant, and its performance was more stable at high pressure compared to the UCO30T membrane containing macrovoids in its substructure. Both tested membranes can, according to the results, also be used at temperatures as high as 70°C in acidic, neutral and alkaline conditions. However, the use at extreme conditions might cause faster ageing of the membranes compared to ageing in neutral conditions. The thesis proved that both the tested RC membranes are very suitable for pulp and paper mill applications and that the membranes can be utilised in processes operating in challenging conditions. Thus, they could be used in more demanding applications than supposed earlier.